Polylactic Acid

Commercial Grade

Poly(lactic acid) or polylactide (PLA) is a thermoplastic aliphatic polyester derived from renewable resources, such as corn starch (in the United States), tapioca products (roots, chips or starch mostly in Asia) or sugarcanes (in the rest of world). It can biodegrade under certain conditions, such as the presence of oxygen, and is difficult to recycle.

PARAMETER                                                                 RESULT

                                                                 Density                                                        1.25 gm/cm³ at 21.5^oC

                                                                Melt Index                                                    5 -7 g/10 min, 190^oC/2.16 kg

                                                                Heat-Deflection-Temperature                 56^oC, 0.455 MPa

                                                                Yield Strength                                             54 Mpa, 5 mm/min.

                                                                Elongation at Break                                    9%

                                                                Flexural Strength                                        104 Mpa, 2 mm/min.

                                                                Flexural Modulus                                       4021 MPa

                                                                Impact Strength                                         4.2 kJ/m², Notched A