CLOISITE Na+ POWDER

Cloisite® Na+ is an additive for plastics to improve various plastic physical properties, such as reinforcement, HDT, CLTE and barrier. 

Physical Properties                         Metric                   English                            Comments

                                   Specific Gravity                               2.8 6 g/cc           2.86 g/cc         

                                   Bulk Density                                    0.1994 g/cc        0.007205 lb/in³                   Loose

                                                                                              0.3356 g/cc       0.01212 lb/in³                       Packed

Loss On Ignition                              7.00 %                  7.00 %             

Particle Size                                  ≤ 2.00 µm            ≤ 2.00 µm                                  10%

                                                                                           ≤ 6.00 µm            ≤ 6.00 µm                                 50%

                                                                                          ≤ 13.0 µm             ≤ 13.0 µm                                   90% 

Mechanical Properties                  Metric                    English                              Comments

Hardness, Shore D                            83                              83                     5% Cloisite® reinforced Nylon 6

Tensile Strength, Ultimate             101 MPa                14600 psi              5% Cloisite® reinforced Nylon 6

Elongation at Break                           8.00 %                        8.00 %            5% Cloisite® reinforced Nylon 6

Modulus of Elasticity                         4.657 GPa             675.5 ksi             5% Cloisite® reinforced Nylon 6

Flexural Modulus                               3.78 GPa                548 ksi               5% Cloisite® reinforced Nylon 6

Izod Impact, Notched                       0.270 J/cm            0.506 ft-lb/in   5% Cloisite® reinforced Nylon 6

 Thermal Properties                        Metric                   English                            Comments

Deflection Temperature at 0.46 MPa (66 psi)      96.0 °C                205 °F                    5% Cloisite® reinforced Nylon 6 

Processing Properties                     Metric                   English                            Comments

Moisture Content                             ≤ 2.00 %                ≤ 2.00 % 

Descriptive Properties

Modifier Concentration,                                                    92.6 meq/ 100g clay           

X-Ray Diffraction d-Spacing (001)                                    11.7 Angstroms